Liqcreate Flame Retardant HDT is a rigid, off-white, self-extinguishing photopolymer that passes UL94 V0, for DLP, LCD and laser-based printers.
Liqcreate Flame Retardant HDT is a rigid, off-white, self-extinguishing photopolymer that passes UL94 V0, for DLP, LCD and laser-based printers.
It combines flame retardance with high temperature resistance and fast printing, for parts in electronics, aviation, automotive and rail.
Values after UV curing for 60 minutes at 60 °C (second figure after 120 minutes) in a high-power LED cure box, from the Liqcreate data sheet.
| Property | Typical value | Test method |
|---|---|---|
| Flammability | UL94 V0 at 3.0 mm | UL94 |
| Tensile strength | 41 MPa (43 MPa after 120 minutes) | ASTM D638M |
| Tensile modulus | 4.2 GPa | ASTM D638M |
| Elongation at break | 1 to 3% | ASTM D638M |
| Flexural strength | 73 MPa (67 MPa after 120 minutes) | ASTM D790 |
| Flexural modulus | 4.3 GPa (4.4 GPa after 120 minutes) | ASTM D790 |
| Impact strength (Izod, notched) | 13 J/m | ASTM D256 |
| Heat deflection temperature at 0.45 MPa | 237 °C (257 °C after 120 minutes) | ISO 75 (HDT-B) |
| Heat deflection temperature at 1.80 MPa | 137 °C (145 °C after 120 minutes) | ISO 75 (HDT-A) |
| Hardness | Shore D 88 (89 after 120 minutes) | ASTM D2240 |
| Degradation temperature | Above 250 °C | Internal method |
| Water sorption | 0.41% | ASTM D570-98 |
| Liquid viscosity at 25 °C | 2,800 mPa·s | - |
Asiga UV series, Nexa3D XiP (open licence), Elegoo, Anycubic and Phrozen series, and open DLP, LCD and SLA printers at 385 to 420 nm.
Complete Fabrication prints parts in Liqcreate Flame Retardant HDT at Lion Works in Whittlesford, near Cambridge, and finishes, paints and assembles them in house. Email your CAD to Info@compfab.co.uk or call +44 1223 836837. We quote fast. If you need a quote quickly, let us know and we will do our best to match your timings. See all materials we run.
Liqcreate Flame Retardant HDT is a rigid, off-white, self-extinguishing photopolymer that passes UL94 V0, for DLP, LCD and laser-based printers.
Liqcreate Flame Retardant HDT has a typical tensile strength of 41 MPa (43 MPa after 120 minutes) (ASTM D638M), according to the Liqcreate data sheet.
The Liqcreate data sheet gives Liqcreate Flame Retardant HDT a heat deflection temperature at 0.45 MPa of 237 °C (257 °C after 120 minutes).
Liqcreate Flame Retardant HDT has a hardness of Shore D 88 (89 after 120 minutes) (ASTM D2240), according to the Liqcreate data sheet.
Liqcreate Flame Retardant HDT is used for interior parts for cars, aircraft, trains and electronic devices, manufacturing aids and tooling, connector housings and covers and parts that must meet UL94 V0.
Yes. Complete Fabrication prints parts in Liqcreate Flame Retardant HDT at its workshop in Whittlesford, near Cambridge. Send CAD to Info@compfab.co.uk. We quote fast, and if you need a quote quickly, let us know and we will do our best to match your timings.
Values are typical figures from the Liqcreate data sheet. They vary with printer, build orientation, post-processing and test method, and are not a specification. Check the current data sheet before you design with the material.
See also:3D printing in Cambridge, all material data sheets and what affects the price. To get parts made in this material, contact us.